THS Heat shrinkable tube for terminals and crimp splices
THS Heat shrinkable tube for terminals and crimp splices
Applications
THS is a heat-shrinkable tube made of polyolefin, and the inner layer is coated with a polyamide hot melt adhesive. Suitable for terminals and crimp joints, providing excellent water and corrosion resistance, fully insulated and protected from electrical connections.
Characteristics Shrinkage ratio 3：1 Abrasion and corrosion resistance Water proof and moisture resistance | Operating temperature range Operating temperature : -55℃～125℃ Minimum shrink temperature : 80˚C fully recovery temperature : 130˚C |
Technical Indicators
Test Item | Characteristics | Test condition | |
Unaged | Tensile strength | Min. 18MPa | Room temp. |
Elongation | Min. 200% | ||
Aged | Tensile strength | Min. 11.5MPa | 158℃/7 days |
Elongation | Min. 100% | ||
Voltage withstand and breakdown Voltage(Unaged) | Withstand 2.5 KV for 1minute and breakdown | Room temp. | |
Voltage withstand and breakdown Voltage(Aged) | Withstand 2.5 KV for 1minute and breakdown at least half of unaged breakdown voltage | 158℃/7 days | |
Copper corrosion | No corrosion of bare copper | 158℃/7 days | |
Copper stability | No sign of degradation Min.Elongation 100% | 158℃/7 days | |
Cold bend | No crack | -30℃/4 hrs | |
Maximum secant modulus(2%) | 250 MPa | - | |
Volume resistivity | Min.1014Ω-cm | - | |
Heat shock | No crack | 250℃/4 hrs | |
Product Dimensions
Part No. | As supplied（mm） | After recovered（mm） | ||
ID | WT | ID(MAX) | WT | |
THS-Φ4.8 | Φ4.8±0.3 | 0.50±0.1 | Φ1.4 | 1.1±0.1 |
THS-Φ5.8 | Φ5.8±0.3 | 0.60±0.1 | Φ1.7 | 1.2±0.1 |
THS-Φ6.8 | Φ6.8±0.3 | 0.65±0.1 | Φ2.1 | 1.4±0.1 |
THS-Φ7.0 | Φ7.0±0.3 | 0.65±0.1 | Φ2.5 | 1.5±0.1 |
THS-Φ8.3 | Φ8.3±0.3 | 0.70±0.1 | Φ3.0 | 1.65±0.1 |